Calcine相关论文
Synthesis,characterization and catalytic performance of nanosized iron-cobalt catalysts for light ol
Nanosized Fe-Co catalysts were prepared by co-precipitation method and studied for the conversion of synthesis gas to li......
Highly active and sintering-resistant heteroepitaxy of Au nanoparticles on ZnO nanowires for CO oxid
Gold was supported on commercial ZnO powders(P) and homemade ZnO nanowires(NWs) by a modified deposition–precipitation ......
Effect of doping rare earth oxide on performance of copper-manganese catalysts for water-gas shift r
Rare earth-doped copper-manganese mixed oxide catalysts were prepared by coprecipitation and mechanical mixing using cop......
M-type Ba hexaferrites were successfully synthesized by sol-gel method. Several synthesizing factors, such as pH value, ......
trimethyl benzene (TMB) was used as organic swelling agent in O/W emulsions to template ul-tra-large mesoporous material......
A novel lanthanum and sulfur co-doped TiO 2 photocatalyst was synthesized by precipitation-dipping method,and characteri......
On June 5th Rain Calcining Limited(RCL)of India and Nanjing Chemical Industry Park Management Committee jointly held a ......
In order to investigate the effect of Ce-doping on the catalysts derived from hydrotalcite-like precursors for carbonyl ......
MgO-CaO/SiO2 solid catalysts derived from waste slag (WS) of metal magnesium plant were prepared. The catalytic performa......
MnFe2O4 polycrystalline powders were prepared by the chemical coprecipitation method. When the reaction temperature is a......
实验研究了氨水的浓度、氨水的用量、氨浸时间、温度对浸出率的影响。称取1g（精确到0．0001g）的矿样，经过最佳条件的焙烧后，最佳浸出条件......
Nanocrystalline SnO2 was synthesized by direct mixing and grinding of SnCl4·5H2O and NaOH at roomtemperature, followed ......
对用于柱色谱分离的填充材料Al2O3,采用清洗、过筛、调节pH值、净化、干燥和活化处理,对获得的Al2O3进行物理性状测试和柱色谱性能......
本文探索了低品位菱镁矿综合利用的新途径.以低品位菱镁矿为原料,在950℃煅烧,研究煅烧时间对低品位菱镁矿失重率的影响,通过正交......
介绍了安徽淮北芦岭煤矿煤系高岭岩的化学及矿物成分,通过生产煅烧高岭岩的试验及生产分子筛的试验,依据国家标准,以芦岭煤矿煤系......
用共沉淀法制备ＺｒＯ２（Ｙ２Ｏ３）超细粉末，在其它工艺相同的条件下，研究了粉末焙烧温度对粉末颗粒度，线性热膨胀和导热性能的影响，证明１２００℃焙烧的粉末制成......
通过煅烧蛋壳获得的高活性冶金石灰，其CaO含量达到95％以上。实验在马弗炉中进行，采用国标法测量石灰活性度。通过正交试验确定石灰活......
采用对比方法研究难冶金精矿焙砂和烟尘氰化浸金的差异。结果表明,直接氰化时焙砂和烟尘中金的浸出率分别为85.31%和54.30%。砷、......
...
本研究以黄铜矿焙砂浸渣为原料，去除有害杂质，加入硫酸制取硫酸铁和硫酸亚铁，再经氧化、水、聚合、获得质量合格的净水剂－－聚合硫酸铁。......
研究了用提钾母液均匀沉淀法获得的70℃烘干的前驱物为原料，直接在620℃下煅烧2h，制备高活性亚微米级MgO粉体材料的方法。根据差热热......
采用低过饱和共沉淀法合成了物质的量比为2，3，4的镁铁水滑石，XRD分析表明它们晶形好，纯度高，以其焙烧产物为催化剂研究了乙酸正丁酯催化......
福建某金精矿焙砂主要组成矿物为赤铁矿与石英，金、银含量分别为31．27g／t、824g／t。采用自主合成的嗜金1号药剂从稀硫酸脱铜后的该金精......
在总结传统的高岭土（岩）增白技术的基础上，着重介绍了酸浸络合除铁增白技术和加增白剂煅烧增白技术，这些技术可除去不同地区高岭土（岩）中......
研究了稀土蓝绿色荧光粉Sr4-x1-x2Bx1Eux2Al14O25 (B = Ca、Sr、Ba,以下简称SBEA)的制备工艺,考察了助熔剂NH4Cl,BaCl2,H3BO3(比例......
Sulfuric acid leaching of high iron-bearing zinc calcine was investigated to assess the effects of sulfuric acid concent......
本文系统地研究了煅烧温度、时间、物料粒度，冷却方式，陈化时间对Ⅱ型无水石膏性能的影响，在中试研究基础上确定了它的工艺制度与参数......
稻壳经稀盐酸煮沸后,用去离子水洗涤至中性,干燥后粉碎并与一定质量的Na2CO3和Al（OH）3粉末混合均匀置于马弗炉中煅烧,煅烧产物采用水......
详细阐述碳酸锂生产新工艺的工艺特点、工艺流程、各步工序操作方法及其注重事项、产品质量水平、技术经济效益等.本文实用性强.......
本文采用变升温速率煅烧和改变煅烧温度探索孔隙形成的特点,同时利用热重分析进行硫化反应,分析煅烧产物的钙转化率,结果表明升温......
本文报导了从贝壳中制取柠檬酸钙的实验原理和操作方法，以及从实验结果得出温度、时间、浓度等的较佳条件．......
羟基磷灰石具有良好的生物相容性,是很好的生物医学植入材料,已得到广泛应用.用于骨组织工程则需要制备具有200～500μm孔径的连通骨......
吉林省地质矿信息中心与白山市八道江区煤管局合作，对山地区石炭、二叠系煤系地层中的硬质高岭（土）岩进行了实验室加工试验，得出了影响......
简要介绍了二位一体煅烧炉的原理、特点和工艺流程，说明了该煅烧炉在砂状冰晶石生产中的应用情况，并与其他干燥设备进行了对比。......
在传统的已工业化天然气A型转化催化剂中加入纳米材料，同时通过考察其成型压力、煅烧温度以及纳米材料添加量对转化催化剂性能的影......
以川西地区微晶白云母为原料,主要研究了在不同的煅烧温度、保温时间、NaOH的浸出浓度、浸出时间、固液比等一系列条件对微晶白云......
我国的钴资源匮乏,因此人们需要有效回收有机钴渣。焙烧渣大多含有高价钴氧化物,需添加SO2或Na2SO3进行还原浸出,其间不可避免地放......
采用共沉淀法合成了9种含铁水滑石，以其焙烧产物为催化剂研究了乙酸正丁酯催化合成的各种影响因素。结果表明：所有焙烧产物都可以催......
以工业氧化锌（ZnO）粉为原料,助剂以四钛酸钾（K_2Ti_4O_9）为主,采用助熔剂法制备大尺寸针状ZnO晶须,并对其生长条件及影响因素进行了研......
以氢氧化钙和氯氧锆为原料，氢氧化钾为矿化剂，在150-250℃和6-12h的水热条件下，制备出粉体前驱物，对该前驱物进行900-1000℃焙烧处理，得......
分析了峙峪矾土的化学组成和矿物组成，研究了不同温度下煅烧矾土，测定 性能和相组成。结果表明，峙峪矾土的主要矿物组成为波美石，含有......
采用D／max-3BX射线衍射仪分析了碳分α-Al（OH）3粉体在200℃～1500℃煅烧过程中的物相转变，研究了煅烧产物的比表面积、安息角、松装密度......
The main technical conditions for synthesizing 4A zeolite with kaolin were determined. The whiteness and calcium ion exc......
A beneficiation-metallurgy combination process is developed to recover Zn, Fe and to enrich In, Ag from high iron-bearin......
转炉钢渣配烧水泥熟料，可降低能耗和成本，提高水泥产量和质量，具有显著的经济效益和环境效益。本文介绍了钢渣配烧水泥熟料的理论依据......
本文考察了氯化铵压煮锂云母焙烧矿的浸出过程,着重研究了压煮温度、时间、液固比、氯化铵配比等因素对锂浸出率的影响,并建立了五......
针对煤系高岭土的特点，探索出一种新型的漂白方法，分析了该方法的作用机理，指出了酸溶氢气法除铁、煅烧除碳是煤系高岭土增白提质的有......
在对传统的高岭土化学漂白方法进行试验比较和研究的基础上，探索出一种新的高岭土漂白方法－酸溶氢气还原法，系统研究了影响漂白效果的......
探讨了微波煅烧仲钨酸铵制取三氧化钨的新工艺。实验结果表明：经微波煅烧4min，仲钨酸铵的分解率为96．67％，并通过正交实验得出微波煅烧的......